Sigma 99 High Performance Packing (PTFE - Graphite Fibre Gland Packing)


ITEM :- Sigma 99

PRODUCT NAME :- Sigma 99 High Performance Packing (PTFE - Graphite Fibre Gland Packing)

BRAND :- SIGMA PLACE OF ORIGIN : INDIA

CERTIFICATION :- API, ISO 9001

APPLICATIONS / USES :-A universal super performance packing made of PTFE(polytetra fluoro ethylene) Graphite filament yarn reinforced with synthetic fibre gland packing Duplex braided interlock construction to increase dimension stability. The combining benefit of PTFE, Graphite & high temperature resisting lubricants gland packing offers the ideal balance between density, resilience , compressibility,strength and durability of the packing.

Product Description
A universal super performance packing made of PTFE(polytetrafluoro ethylene) Graphite filamentfibre yarn. Duplex braided interlock construction to increase dimension stability. The combining benefit of PTFE, Graphite & high temperature resisting lubricants gland packing offers the ideal balance between density, resilience, compressibility,strength and durability of the packing.

A high performance packing is recommended for oil & solvents, caustics, acids, dyes, chemicals, chlorinated water, white and black liquor, wood pulp, detergent, alkalies, hydrocarbons, inorganic chemical handling equipments, steamvalvess, metering pumps, reactors, mixers, autoclave glands, bauxite slurries, bottom ash slurry pumps, mineral handling slurries, tailings pumps and other slurry processing applications. Not recommended to use in strong oxidising agents, aqua regia fluorine, fuming nitric acid, oleum and molten alkali metals.


Service Limits, Application Parameter

Specifications
Pressure Psi bar
to 300 psi (20 bar) rotary/ centrifugal; to 2000 psi (138 bar) valves
Shaft speed M/s
to 3000 rpm
Density g/cm3
1.5
Temperature °C
-2000F (-1300C) to +5500F(+2880C)
PH range
0-14

Size Dimensions

Size mm
4
5
6
8
10
12
14
15
16
18
19
20
approx. mtr. / kg
35
22
16
9.0
5.6
3.9
2.9
2.5
2.2
1.7
1.5
1.4

Prime Features

  • Extended service life by up to 400% in harsh environments
  • Well proven with aggressive media
  • High thermal conductivity for cool running.
  • Low coefficient of friction and minimal shaft wear.
  • Very good start-up and emergency running characteristics.
  • Less gland adjustment, easy break-in, & even compression in all rings
  • Six times better heat conduction as against pure PTFE packings at comparatively high speeds.
  • ignificantly low thermal expansion thus resisting ‘ over expansion’ extrusion under service.
  • The packing does not harden and runs cool.
  • It has low co-efficient of thermal expansion.
Our motto is to provide best international quality products at very competative price.